This set of Vero materials is rigid and opaque, with a high level of surface detail and available in multiple colors. These PolyJet materials are general-purpose resins, offering enhanced mechanical properties and the ability to withstand bending. We offer opaque colors in the Vero line. These materials can be blended with others on PolyJet machines to achieve your desired level of rigidity or translucency.
Technical Specifications
| Standard lead time | Minimum of 3 working days (offline orders) 4 working days (online orders) |
| Standard accuracy | 0.1 – 0.3 mm (varies depending on geometry, part orientation and print size) |
| Layer thickness | 0.032 mm |
| Minimum wall thickness | 1 mm |
| Maximum part dimensions | 490 x 390 x 200 mm (offline orders) 350 x 250 x 100 mm (online orders) |
| Interlocking or enclosed parts? | Yes |
| Surface structure | Unfinished PolyJet parts have a smooth surface, which can be further smoothed as desired through finishing processes. |
Datasheet
| MEASUREMENT | VALUE | STANDARD |
|---|---|---|
| Tensile Strength | 50 – 65 MPa | ASTM D-638 |
| Elongation at Break | 10 – 25% | ASTM D-638 |
| Modulus of Elasticity | 2000 – 3000 MPa | ASTM D-638 |
| Flexural Strength | 75 – 110 MPa | ASTM D790 |
| Flexural Modulus | 2200 – 3200 MPa | ASTM D790 |
| Notched Izod Impact | 20 – 30 J/m | ASTM D256 |
| Shore Hardness (D) | 83 – 86 | Scale D |
| Rockwell Hardness | 73 – 76 | Scale M |
| Heat Deflection Temperature | 45 – 50°C 45 – 50°C |
ASTM D648 @ 0.45 MPa @ 1.81 MPA |
| Glass Transition Temperature | 52 – 54°C | DMA, E" |
| Ash Content | 0.23 – 0.26% | USP281 |
| Polymerized Density | 1.17 – 1.18 g/cm³ | ASTM D792 |
Actual values may vary with build condition. Shore values are provided by Stratasys.
How Does PolyJet Work?
PolyJet works by jetting photopolymer materials in ultra-thin layers onto a build platform. Each photopolymer layer is cured by UV light immediately after it is jetted, producing fully cured models that can be handled and used immediately, without post-curing. The gel-like support material, designed to support complicated geometries, is subsequently removed by water jetting.