VeroClear is a transparent, rigid material that offers exceptional surface detail, in common with the Vero family of materials. The high dimensional stability and smooth surface quality of VeroClear make it an ideal material for fine-detailed model building, or prototypes for clear parts. With its transparent appearance, VeroClear is also ideal for parts which require visibility of liquid flows. To create an endless variety of translucent shades or patterns, VeroClear can be combined with colored materials on PolyJet machines.
Technical Specifications
| Standard lead time | Minimum of 5 working days |
| Standard accuracy | 0.1 – 0.3 mm (varies depending on geometry, part orientation and print size) |
| Layer thickness | 0.032 mm |
| Minimum wall thickness | 1 mm |
| Maximum part dimensions | 490 x 390 x 200 mm (offline orders) 350 x 250 x 100 mm (online orders) |
| Interlocking or enclosed parts? | Yes |
| Surface structure | Unfinished PolyJet parts have a smooth surface, which can be further smoothed as desired through finishing processes. |
Datasheet
| MEASUREMENT | VALUE | STANDARD |
|---|---|---|
| Tensile Strength | 50 – 65 MPa | ASTM D-638 |
| Elongation at Break | 10 – 25% | ASTM D-638 |
| Modulus of Elasticity | 2000 – 3000 MPa | ASTM D-638 |
| Flexural Strength | 75 – 110 MPa | ASTM D790 |
| Flexural Modulus | 2200 – 3200 MPa | ASTM D790 |
| Notched Izod Impact | 20 – 30 J/m | ASTM D256 |
| Shore Hardness (D) | 83 – 86 | Scale D |
| Rockwell Hardness | 73 – 76 | Scale M |
| Heat Deflection Temperature | 45 – 50°C 45 – 50°C |
ASTM D648 @ 0.45 MPa @ 1.81 MPA |
| Glass Transition Temperature | 52 – 54°C | DMA, E" |
| Ash Content | 0.02 – 0.06% | USP281 |
| Polymerized Density | 1.18 – 1.19 g/cm³ | ASTM D792 |
Actual values may vary with build condition. Shore values are provided by Stratasys.
How Does PolyJet Work?
PolyJet works by jetting photopolymer materials in ultra-thin layers onto a build platform. Each photopolymer layer is cured by UV light immediately after it is jetted, producing fully cured models that can be handled and used immediately, without post-curing. The gel-like support material, designed to support complicated geometries, is subsequently removed by water jetting.